Vasile et al. zig'ir va kanop–zig'ir to'qima matosining shimsimon namunalarini yirtdi, polotno o‘rilishida, panama va sarja o‘rilishlari, cho‘zilish sinov qurilmasida, va qayd etadilar: “Eng past yirtilish kuchi ham nasha–zig'ir, ham zig'ir matolar holatida polotno to'qima uchun qayd etildi.”
Hossain et al ning ANOVA tahlili yirtilish mustahkamligini nima belgilashini aniqladi, va cho'zilish mustahkamligini nima belgilaydi, ichida 100% paxtali to'qima mato?
Tanda yoʻnalishida yirtilish uchun, Hossain va boshq. yozish: “Mato dizaynining asosiy ta'siri sezilarli, F(7,14)=2.89, p=0.04; ya’ni tanda yo‘nalishidagi o‘rtacha yirtilish mustahkamligi (Y1) dizayndan dizaynga sezilarli darajada farq qiladi”. To'quv dastgohi sozlamasi bunday ta'sir ko'rsatmadi: “Jadval 3 to‘quv dastgohi sozlamasining asosiy ta’siri ahamiyatsiz ekanini ko‘rsatadi, F(2,14)= 0.92, p=0.42, bu esa o'rtacha tanda yo'nalishidagi yirtilish mustahkamligi (Y1) to‘quv dastgohining uchta sozlamasi uchun deyarli bir xil.”
Arqoq yo'nalishidagi yirtilish ham xuddi shunday davom etdi. Toʻquv dastgohini sozlash uchun, “to‘quv dastgohi sozlamasining asosiy ta’siri sezilarli emas, F(2,14)=1.59, p=0.24”. Toʻqima uchun, “mato dizaynining asosiy ta'siri ahamiyatlidir, F(7,14)=3.20, p=0.03”.
Cho'zilish mustahkamligi esa aksincha bo'ldi. “To'quv dastgohi sozlamasining asosiy ta'siri juda muhimdir quyidagi unumdorlikda: Y3, F(2,14)=316.9, p=0.00.” Toʻqima uchun, “mato dizaynining ta’siri ahamiyatsiz; tanda yo‘nalishidagi cho‘zilish mustahkamligining o‘rtacha qiymati (Y3) bir xil to‘quv dastgohi sozlamasidagi sakkizta dizayn uchun deyarli bir xil, F(7,14)=2.07, p=0.12.”
Paxta namunalari bitta paxta ipidan sakkizta to'qima dizaynida to'qilgan, har biri to‘quv dastgohining uchta sozlamasida (turli barda va remiz raqamlari), namuna rapirali to‘quv dastgohida. Yirtilish fermentativ ohordan tozalashdan so'ng Elmendorf tipidagi mayatnikli sinov uskunasida o'lchandi, yuvish, quritish va bo‘shashtirish. Ohordan tozalash bir nechtadan biridir paxta uchun fermentli ishlovlar.
Hossain et al ning paxta matolarida qaysi to'qima eng qiyin yirtildi, va mualliflar buni nima bilan izohlaydilar?
Hossain va boshq. yozish: “Rogojka matosining yirtilish mustahkamligi reps matosidan yuqoriroq, tvil, va satin, o'xshash to'quv o'tish uzunligi bilan (Rasm. 5).” Tanda bo'yicha yirtilish uchun ularning ANOVA tahlilida, “tanda yo‘nalishidagi yirtilish mustahkamligining eng yuqori o‘rtacha qiymati (Y1) dizayn uchun olingan edi 2 xira polotno.”
Mualliflar buni erkin o'tish uzunligi hamda tanda va arqoqning kesishish usuli bilan bog'laydilar. “Suzish uzunligiga koʻra, matodagi suzma uzunligi yirtilishga chidamlilikka sezilarli ta’sir qiladi, deb aytish mumkin. Ip tashlamasi uzunligining oshishi bilan, ko‘proq iplar bir-biriga yaqin joylashadi, shu tariqa yirtilish mustahkamligini oshiradi.” Ular qo'shimcha qiladilar: “Shunday qilib, o'qoq va arqoq iplari orasidagi aloqa, to'qilish shakli yoki to'qima dizaynidagi o'zgarishlar o'qoq va arqoq bo'yicha yirtilish mustahkamligida muhim rol o'ynaydi”.
Faqatgina suzish uzunligi A jadvaldagi paxta natijalari tartibini tushuntirmaydi. Satin uchta ip ustidan erkin o'tadi; muntazam panama to'qimasi ustidan o'tadigani ikki. Biroq, o'qoq yo'nalishida to'quv dastgohining eng zich sozlamasida, satin ikkala mat to'qimasidan va ikkinchi tanda ripsidan ko'ra pastroq kuchda yirtildi.
Mualliflar shuningdek shuni yozadilarki “mustahkamlik remizlar soni ortishi bilan ortadi”. Ularning diagrammalari buni polotno to'qimaga nisbatan o'zgarish sifatida o'lchaydi, nyutonlarda emas: “Tekis toʻqimaga nisbatan arqoq yoʻnalishidagi yirtilish mustahkamligining kasrli oʻzgarishi.” Nyutonlarda, satin va ikkala diagonal to'qima eng zich sozlamada boshqa ikki sozlamaga qaraganda pastroq kuchda yirtildi.
Eng zich sozlamada tanda yo'nalishidagi noto'g'ri rogojka ko'rsatkichi yirtilish sinov uskunasining ko'rsatilgan quvvatiga yaqin, mualliflar shunday keltirgan “Maksimal yuk bilan Elma Tear 133 N”. Shu sababli, bu aniq qiymat bo‘lmasligi mumkin.
| To'quv dastgohi sozlamasi | Dizayn | Law bo'yicha maksimal ip zichligi | EPCm | PPCm | O'qoq bo'yicha yirtilish (N) | Arqoq bo'yicha yirtilish (N) |
|---|---|---|---|---|---|---|
| Tishli taroq 60/gulbosh 30 | Oddiy | 22 | 15 | 14 | 56.390 | 64.011 |
| Tishli taroq 60/gulbosh 30 | Tekis tanda reps to'qimasi | 30 | 14 | 14 | 92.132 | 78.373 |
| Tishli taroq 60/gulbosh 30 | (2) Tekis to'g'ri rogojka | 30 | 16 | 13 | 100.950 | 103.010 |
| Tishli taroq 60/gulbosh 30 | Tekis tanda reps to'qimasi | 33 | 15 | 14 | 62.296 | 76.838 |
| Tishli taroq 60/gulbosh 30 | (3+1) Tekis noto'g'ri rogojka | 33 | 17 | 14 | 75.424 | 70.724 |
| Tishli taroq 60/gulbosh 30 | Z-sarja | 30 | 16 | 14 | 80.386 | 88.242 |
| Tishli taroq 60/gulbosh 30 | Z-sarja | 33 | 15 | 14 | 84.252 | 88.754 |
| Tishli taroq 60/gulbosh 30 | Satin | 33 | 17 | 14 | 81.405 | 92.152 |
| Tishli taroq 40/gulbosh 40 | Oddiy | 22 | 19 | 17 | 39.681 | 48.406 |
| Tishli taroq 40/gulbosh 40 | Tekis tanda reps to'qimasi | 30 | 21 | 18 | 105.640 | 85.288 |
| Tishli taroq 40/gulbosh 40 | (2) Tekis to'g'ri rogojka | 30 | 20 | 17 | 106.390 | 102.505 |
| Tishli taroq 40/gulbosh 40 | Tekis tanda reps to'qimasi | 33 | 20 | 18 | 108.470 | 84.684 |
| Tishli taroq 40/gulbosh 40 | (3+1) Tekis noto'g'ri rogojka | 33 | 21 | 18 | 93.060 | 95.304 |
| Tishli taroq 40/gulbosh 40 | Z-sarja | 30 | 20 | 18 | 96.719 | 100.558 |
| Tishli taroq 40/gulbosh 40 | Z-sarja | 33 | 20 | 18 | 83.534 | 90.806 |
| Tishli taroq 40/gulbosh 40 | Satin | 33 | 21 | 18 | 72.418 | 85.810 |
| Tishli taroq 60/gulbosh 60 | Oddiy | 22 | 25 | 24 | 18.858 | 32.798 |
| Tishli taroq 60/gulbosh 60 | Tekis tanda reps to'qimasi | 30 | 26 | 25 | 63.872 | 56.667 |
| Tishli taroq 60/gulbosh 60 | (2) Tekis to'g'ri rogojka | 30 | 25 | 25 | 100.408 | 104.193 |
| Tishli taroq 60/gulbosh 60 | Tekis tanda reps to'qimasi | 33 | 26 | 25 | 122.200 | 64.117 |
| Tishli taroq 60/gulbosh 60 | (3+1) Tekis noto'g'ri rogojka | 33 | 27 | 26 | 132.810 | 129.400 |
| Tishli taroq 60/gulbosh 60 | Z-sarja | 30 | 26 | 26 | 59.613 | 72.977 |
| Tishli taroq 60/gulbosh 60 | Z-sarja | 33 | 26 | 25 | 47.421 | 48.136 |
| Tishli taroq 60/gulbosh 60 | Satin | 33 | 27 | 26 | 41.407 | 71.366 |
Vasile et al.ning zig'ir va nasha–zig'ir shim shaklidagi yirtilish namunalari qaysi yo'nalishda ko'ndalangiga yirtilmadi?
Vasile et al. hisobot: “Sinov davrida, har bir matoning barcha beshta namunasi o'qoq yo'nalishida yirtildi. Aksincha, arqoq yo‘nalishida, beshta FLAX PLAIN namunasi, uchta ZIG'IR DIAGONAL va KANOP POLOTNO namunasi, va HEMP PAN ning hech bir namunasi, KENEVIR SARJA, va FLAX PAN ushbu yo'nalish bo'ylab ko'ndalangiga yirtildi.”
Oltita mato sanoat to'quv dastgohida to'qilgan. Barchasi umumiy oqartirilgan zigʻirga ega (zig'ir) burish. Arqoq esa zig'irdan iborat, zig‘ir matolariga berib (ZIGʻIR), yoki kanop, kanop–zig‘ir matolariga berib (KENEVIR). Har bir arqoq tekis toʻqima sifatida toʻqilgan, panama (PAN) yoki sarja.
Tadqiqotchilar dastlab mayatnikni sinab ko'rishdi (Elmendorf) ushbu zig‘ir va kanop–zig‘ir matolarida yirtilish sinovi. “Ushbu urinish muvaffaqiyatsiz tugadi, chunki namunani yirtish uchun zarur bo'lgan kuch asbob tomonidan ko'rsatilgan maksimal kuchdan oshib ketdi.” Keyin ular shimsimon namunadan foydalanishdi: yoriqli tasmacha, ikkita oyog'i cho'zilish sinagichida bir-biridan ajratilgan.
Vasile et al ning zig'ir va kanop-zig'ir matolarida o'tkazgan Martindale ishqalanish sinovida qaysi to'qima birinchi bo'lib yeyildi?
Vasile et al. yozish: “Tahlil qilingan oltita mato orasida, panama to'qimasi polotno va ayniqsa diagonal to'qimalarga nisbatan ishqalanishga eng sezgir bo'lgani aniq edi.” Arqoq tolasida, ular shunday yozadilar: “Bir xil to'qimaga ega gazlamalar ishqalanishga bir xil darajada chidamli ekanligi kuzatildi, arqoq turidan qat’i nazar.”
| Mato | Arqoq | Toʻqish | Buzilishgacha boʻlgan davrlar |
|---|---|---|---|
| KENEVIR TEKIS | Kenevir | Oddiy | 5000 |
| KENEVIR PANAMA | Kenevir | Panama | 4000 |
| KENEVIR SARJA | Kenevir | Sarja | 6000 |
| ZIGʻIR TEKIS | Zig'ir | Oddiy | 5000 |
| ZIGʻIR PANAMA | Zig'ir | Panama | 4000 |
| ZIGʻIR SARJA | Zig'ir | Sarja | 6000 |
Vasile et al. bu natijani faqat “qisman mos” oldingi tadqiqotlar bilan, bu esa “sarja va atlas o‘rilishlarida polotno va panamaga qaraganda ko‘proq ishqalanish qayd etilgan, dastlabki ikkita to'qimaning uzunroq tashlama iplari bilan izohlandi.” Sarjada, ikkala natija bir-biriga mos kelmaydi: avvalgi ishda sarjada ko‘proq ishqalanish aniqlangan, Vasile et al.ning Martindale sinovida diagonal eng uzoq chidagan bo'lsa-da.
Manbalar: Hossain, M. M., Alimuzzaman, S. & Ahmed, D. M. (2023). “Yirtilish va cho'zilish mustahkamligi 100% Paxtali toʻqima matolar’ Asosiy tuzilmalar: Regressiya modellashtirish”. Tolalar va toʻqimachilik 30(2), 14–25. DOI 10.15240/tul/008/2023-2-002. https://dspace.tul.cz/items/cc620c63-5386-4717-96e9-403bb1c2fa2e/full. Vasile, S., Vermeire, S., Vandepitte, K., Troch, V. & De Raeve, A. (2024). “Toʻqima va arqoq turining kenevir–zigʻir matolarining mexanik va qulaylik xususiyatlariga taʼsiri”. Materiallar 17(7), 1650. DOI 10.3390/ma17071650. https://pmc.ncbi.nlm.nih.gov/articles/PMC11012718/.
Ayollar kiyimlari assortimentini ishlab chiqish? Biz qanday ishlayotganimizni ko'ring Hindistonda ayollar kiyimlari ishlab chiqaruvchisi.
B2B lukbuklarini ko'ring → bizning eng so'nggi to'plamlarimizdan bir ko'rinish. To'liq diapazonni talab qiling: so'rov bo'yicha ko'proq dizaynlar.